Color | WHITE | |||
---|---|---|---|---|
Type | 4 | |||
ADA Class | NOBLE (N) | |||
Application |
Investment | Phosphate Bonded (Carbon Free) |
---|---|
Crucible | Ceramic |
Degassing Temp C | 650-1010 |
Oxidation Procedure | hold 5 min, remove oxide, no vacuum |
PreSolder | WSF |
---|---|
PostSolder | LO, 500 |
Laser Wire | LWT80 |
Gold (AU) | 1.8 |
---|---|
Platinum (PT) | 0 |
Palladium (PD) | 75.7 |
Silver (AG) | 0 |
Copper (CU) | 7.5 |
Zinc (ZN) | 0 |
Tin (SN) | 0.2 |
Indium (IN) | 8 |
Gallium (GA) | 6.3 |
VHN After Firing | 290 |
---|---|
VHN Soft | --- |
VHN Hard | 315 |
Proof Stress Soft MPa | 700 |
Proof Stress Hard MPa | 950 |
Tensile Strength Soft MPa | 1201 |
Tensile Strength Hard MPa | 1310 |
Elongation Soft | 19 |
Elongation Hard | 16 |
Elastic Modulus GPa | 130 |
Melting Range C | 1150-1180 |
---|---|
Casting Temp C | 1290 |
Density g/cc | 11.2 |
Expansion at 500C | 14.1 |
Expansion at 600C | 14.3 |
Burnout Temp C | 815 |